Material :1cr17ni2
Ingredients:
C Si Mn P S Cr Ni Mo V Cu Nb Ti N
0.11 to 0.17 ≤0.8 ≤0.8 ≤0.040 0.03 16 to 18 1.5 to 2.5
Delivery condition: Annealed HB≤285
Method of steelmaking:
Table 4-21-5 Hot working technology of 1Cr17Ni2 steel
Loading furnace temperature Start temperature /℃ End temperature /℃ cooling condition
Cold loading furnace temperature ≤800℃, hot loading furnace temperature is not limited to 1100~1150 >850 >150 slow cooling in the sand
(1) Extracted from GB/ T1120-1992. the hardness is the value after annealing or high temperature tempering;
② Actual production inspection value.
Item Heating temperature /℃ Cooling tissue annealing HB
σb/MPa δ5/% aK/J·cm-2
Note:
Annealing 670 furnace cold pearlite ≤285 quenching and tempering mechanical properties ≥1100 ≥10 ≥50 HRC49-54 ①
Quench 950~975 oil martensite 187~286
1100 10~22 50~25 ②
Tempering 275~300 oil martensite
~ 1730
Uses: Molds, accessories, plastic molds, corrosion resistance and mirror rust prevention mold, etc. 1Cr17Ni2 series is a kind of steel with good strength and toughness in martensitic stainless steel. It has good corrosion resistance to aqueous solutions of oxidizing acids, most organic acids and organic salts. Generally suitable for the manufacture of nitric acid, acetic acid production and light industry, textile and other industries require both strong toughness and corrosion resistance of the shaft, piston rod, pump and other parts.